... basic formula基本配方 curing process固化过程 a key element of “photoinitiator”关键成分光引发剂 ...
基于28个网页-相关网页
高密度环氧泡沫塑料的制备工艺及性能研究 关键词：环氧泡沫塑料；高密度；固化工艺；力学性能 [gap=972]Key words：epoxy foam；high—density；curing process；mechanical property
基于20个网页-相关网页
... 固化处理 curing process; solidification process 固化点 solidification point 固化范围 {化} solidification range ...
基于4个网页-相关网页
Steam Curing Process 蒸汽交联工艺
Radiant Curing Process 辐照交联工艺
Flue curing process 烘烤过程
high temperature steam-curing process 高温汽蒸焙烘法
curing process of the underfill 底充胶固化工艺
UV curing process 紫外曝光固化工艺
the curing process 烘烤过程
rapid curing process 快速固化工艺
The curing process was 100℃/2h+150℃/2h+200℃/1h, the values of apparent activation energy and reaction order were 65.68kJ/mol and 0.898 respectively. When the ratio of SNA and CER-170 was 80 to 100, the gel time was the shortest.
SNA固化环氧树脂CER-170时用量为80份时凝胶时间最短,110份时固化最完全,固化工艺为80℃/2h+120℃/2h+150℃/2h+220℃/2h,固化反应的表观活化能Ea=87.3kJ/mol,反应级数n=0.9226。