The results show that main cause of conchoidal fracture forming is that composition segregation in solidification grain boundary of casting steel reduces the resistance of crack propagation.
结果表明，沿一次晶晶界的成分偏析对裂纹扩展阻力的降低作用是铸钢中贝壳状断口形成的主要原因。
The relationship between the boron hardenability factor and the equilibrium segregation of boron to grain boundary, the composition of steel, the austenitizing temperature, grain size was studied.
研究了硼淬透性因子与硼的晶界平衡集聚规律、钢的成分、奥氏体化温度及晶粒尺寸的关系。建立了硼的晶界平衡集聚方程。