Through the discussion on the mechanism and effect factors of the stress corrosion cracking by sulfides, this paper expounds its harmfulness and proposes some measures to control it.
本文通过对硫化物应力腐蚀开裂的机理和影响因素的讨论,说明其危害性并提出了控制方法。
The mechanism of the shat-blast enhancing technology and its eldest on improving resisfemle to fatigue and stress corrosion fracture are describe briefly in this paper.
本文简要介绍喷丸强化工艺的机理,及在改善金属零部件疲劳断裂和应力腐蚀断裂抗力中的强化效果;
The stress corrosion mechanism in mixed solutions was studied based on the metallographic observations of scanning fracture shapes and crack extension direction.
根据扫描断口形貌和裂纹扩展途径的金相观察,还探讨了在混合溶液中的应力腐蚀机制。