Compared to the matrix resin,this nano hybrid resin has shown reduction of volume shrinkage 38% and increase of tensile strength 31%.
该纳米复合树脂与基体树脂相比较,体积收缩率降低38%,拉伸强度提高31%。
参考来源 - 紫外光固化纳米复合树脂的制备·2,447,543篇论文数据，部分数据来源于NoteExpress
With crystalline plastics this can be significant as volume shrinkage is high.
对于结晶塑料，这种压力是巨大的，因为它的体积收缩高。
Polymerization volume shrinkage of EEPE resin was lower than other dimethacrylate resin.
与其他甲基丙烯酸类树脂相比，EEPE树脂的聚合收缩率比较低。
The volume shrinkage of the sample was lowed from 7% to 0.8%, which apparently smoothen the film.
特别是树脂的固化体积收缩率显著降低，从7％下降到0.8％，明显改善了涂膜的平整性。