The results show that the crack growth rate under high-low cycle complex fatigue load is greater than that under low cycle fatigue load, and so the fatigue life is obviously reduced.
结果表明：与纯低周载荷作用相比，高低周复合载荷下球墨铸铁的裂纹扩展速率明显加快，极大地降低材料的疲劳寿命。
The fretting fatigue life under complex loads monotonously decreases with the increase of the high cycle load while the low cycle loads keep constant.
复合载荷下，低周幅值不变，增加高周载荷的幅值，微动疲劳寿命随幅值比的增加而降低。